Elongational properties and molecular structure of polyethylene melts

The viscosity and the recoverable strain in the steady state of elongation have been measured on several polyethylenes of different molecular structures. The elongational viscosity as a function of tensile stress runs through a more or less pronounced maximum in the nonlinear range whereas in the linear range the Trouton viscosity is reached. For low density polyethylenes it could be demonstrated that the maximum of the steady-state elongational viscosity and the elasticity expressed by the steady-state compliances in shear and tension sensitively increase if the molecular weight distribution is broadened by the addition of high molecular weight components. A variation of the weight average molecular weight does only shift the elongational viscosity curve but leaves its shape unchanged. Two of the four high density polyethylenes investigated do not show a maximum of the steady-state elongational viscosity, for the others it is less pronounced than in the case of low density polyethylenes. The influence of branching on the elongational behaviour of polyethylene melts in the steady-state and the transient region is qualitatively discussed.