Effect of polarization on the electrode behavior and microstructure of (La,Sr)MnO3 electrodes of solid oxide fuel cells

The electrode behavior and microstructure of freshly prepared (La0.8Sr0.2)0.9MnO3 (LSM) electrodes were investigated under various polarization conditions. The original, large agglomerates in freshly prepared LSM electrodes were broken down into sphere-shaped grains when exposed to cathodic or anodic current passage of 200 mA cm−2 at 800 °C in air for 3 h. Microstructural changes under cathodic polarization could be related to the pronounced diffusion and migration of oxygen vacancies and Mn ions on the LSM surface and lattice expansion, while lattice shrinkage under oxidation conditions most likely contributes to the structural changes under anodic polarization. Such morphological changes were irreversible and were found to be beneficial to the performance of freshly prepared LSM electrodes. Freshly prepared LSM electrodes behaved very differently with respect to the cathodic and anodic current passage treatment.