Magnetic and interface properties of the core-shell Fe3O4/Au nanocomposites

Core-shell Fe3O4/Au nanostructures were obtained with an advanced method of two step synthesis and several complementary methodics were applied for investigation structural and magnetic properties of the samples. Along with X-ray diffraction and transmission electron microscopy, electron diffraction, optical, Raman and Mossbauer spectroscopy were used for nanoparticle characterization. It was established that the physical and structural properties Fe3O4/Au nanocomposites are specific of intrinsic properties of gold and magnetite. Mossbauer and Raman spectroscopy data indicated that magnetite was in a nonstoichiometric state with an excess of trivalent iron both in the initial Fe3O4 nanoparticles and in the Fe3O4/Au nanocomposites. As follows from the Mossbauer data, magnetic properties of iron ions in the internal area (in core) and in the surface layer of magnetite nanoparticles are different due to the rupture of exchange bonds at the particles surface. This leads to decrease in an effective magnetic moment at the surface. Gold atoms at the interface of the composites interact with dangling bonds of magnetite and stabilize the magnetic properties of the surface layers of magnetite.