Effects of synthesis-solvent on swelling and elastic properties of poly(N-isopropylacrylamide) hydrogels

Thermosensitive N-isopropylacrylamide (NIPA) hydrogels were synthesized by a free radical copolymerization with N,N′-methylenebisacrylamide (MBAA) in four solvents: water, ethanol, acetone and N,N-dimethylformamide. The swelling and elastic properties of the hydrogels were affected by the synthesis-solvents; the hydrogels (e.g. NIPA/MBAA = 1000/50 mol/m3-pre-gel solution) synthesized in water have smaller swelling volume and larger shear modulus at 10 °C than those synthesized in amphiphilic solvents. The network structure of hydrogels was estimated in terms of the conversion and two sorts of effective crosslinking density based on the Flory theory and the concentration of crosslinker. The hydrogels synthesized in water can have the microscopic inhomogeneous network arising from the entanglement of polymer chains, while the hydrogels synthesized in amphiphilic solvents can have the homogeneous network arising from the polymer concentration lower than the pre-gel solution and can be similar in network structure to the lightly crosslinked hydrogel synthesized in water.