Fabrication of moldable chitosan gels via thermally induced phase separation in aqueous alcohol solutions

Wide application of chitosan in modern technologies is limited by the lack of reliable and low-cost techniques to prepare size-tuned constructs with a complex surface morphology, improved optical and mechanical properties. We report a new simple method for preparation of transparent thermoreversible chitosan alcogels from chitosan/H 2 O/ethanol ternary systems. This method, termed “low temperature thermally induced phase separation under non-freezing conditions” (LT-TIPS-NF), fine tunes gelation by adjusting only temperature (from 5 to −25 °C) and varying the initial content of chitosan (from 0.5 to 2.0 wt%) and ethanol (from 28.5 to 47.5 vol%). Transparent non-swelling final constructs of complex shape are prepared by fixing the pre-formed alcogels with a base solution. The size of the gel constructs is limited only by the dimensions of the mold and the cooling chamber. The LT-TIPS-NF is applicable both in injection molding and 3D printing techniques. The in vitro and in vivo experiments show the absence of prominent cytotoxicity and well-defined cell adhesion on the obtained hydrogels. Thus, this facile and scalable technique provides the multifunctional chitosan gel preparation with easily controlled properties exploiting inexpensive, renewable, and environmentally friendly source polysaccharide. These materials have prospects for a variety of uses, especially for biomedical applications. • An approach for thermoreversible chitosan-based alcogel formation by LT-TIPS-NF method was developed. • Nanofibrous hydrogels with high transparency and increased mechanical strength were fabricated by fixation of alcogels. • Molding and 3D-printing of hydrogel constructs with complex structure morphology was performed. • The prepared hydrogels demonstrated good cell viability in vitro and high biocompatibility in vivo.