Cation Mobility and Kinetics of Ion Exchange in Zirconium Hydrogen Monothiophosphate Hydrate, Zr(HPO₃S)₂·1.5H₂O

The ion conductivity of zirconium hydrogen monothiophosphate (Zr(HPO(3)S)(2)x1.5H(2)O) has been measured by impedance spectroscopy. The measured value of proton conductivity is 3 x 10(-5) S/cm at 298 K. Conductivity was shown to decrease with increasing temperature due to a dehydration process. Above 450 K, the conductivity is likely governed by proton transport in the anhydrous phase Zr(HPO(3)S)(2). The activation energies of proton conductivity were measured to be 18 +/- 2 kJ/mol for Zr(HPO(3)S)(2)x1.5H(2)O and 60 +/- 3 kJ/mol for the anhydrous compound. The kinetics of ion exchange was studied with the use of potentiometric titration for several ion pairs, H(+)/Na(+), H(+)/Zn(2+), and Na(+)/Zn(2+) in Zr(HPO(3)S)(2)x1.5H(2)O. The diffusion coefficient values for H(+)/Na(+) ion exchange in Zr(HPO(3)S)(2)x1.5H(2)O are lower than those reported in alpha-zirconium phosphate. At the same time, the mobility of zinc ions in Zr(HPO(3)S)(2)x1.5H(2)O is higher than sodium ion mobility. The ion exchange H(+)/Zn(2+) is accompanied by the slow hydrolysis of the initial compound. In all cases, the powdered solids were evaluated by powder X-ray diffraction, and particle sizes were controlled by grinding and sieving the powders.