Synthesis and Properties of a Carbon Monoxide Oxidation Catalyst Based on Titanium Dioxide and Platinum Nanoparticles

Carbon monoxide oxidation catalysts comprising Pt clusters on titanium dioxide with an oxide particle size of 6 and 20 nm have been synthesized. The catalysts have been studied using TEM, XRD, and XPS techniques, and it has been found that platinum clusters coated with a mixture of platinum oxides are formed on the support surface. The coherent scattering region of the Pt cluster is close to 5–6 nm for the studied oxide supports. The catalytic properties in the CO oxidation reaction at 295 K and low CO concentrations (less than 100 mg/m3) have been examined. The catalyst based on titania with a particle size of 20 nm and a platinum loading of 10 wt % has been found to have the CO oxidation rate 100 times higher than that on platinum black with a specific surface area of 30 m2/g. The catalysts are promising for use in catalytic air purification systems.