Solubility of vanadium from manganese vanadates in aqueous solutions of soda ash

It is shown that, in the course of developing the technology of pure vanadium pentoxide preparation from manganic vanadium-containing metallurgical slags, their oxidative roasting and cinder formation without alkaline additives are accompanied by the decomposition of spinelides with the formation of manganese meta- and pyrovanadates. Concentrated aqueous solutions of soda ash with an Na2CO3 concentration of 120–150 g/dm3 are accepted as a selective leaching reagent for vanadium from a cinder. Manganese metaand pyrovanadates are synthesized, and the procedure of their preparation is presented. The solubility of vanadium from manganese vanadates in aqueous solutions of soda ash at $$C_{Na_2 CO_3 } = 150 g/dm^3 $$ is studied at 20–95°C for pyrovanadate and at 85–95°C for metavanadate. It is shown that vanadium should be leached from converter manganic slags roasted without alkaline metal additives at a leaching solution temperature higher than 95°C. There is a possibility to increase the vanadium content in a leaching solution to 60–80 g/dm3. The results obtained are used in the development of the technology of vanadium leaching.