Microstructure and electrochemically active surface area of PtM/C electrocatalysts

The results of the study of microstructural parameters and the data on the electrochemically active surface area of Pt/C and Pt50M50/C (M = Ni, Cu, Ag) catalysts in 1 M H2SO4 solutions are compared. The metal-carbon nanomaterials were prepared by the method of chemical reduction of metals from the organoaqueous solutions of their compounds. The loading of metal component in them was 30–33 wt %. It is found that actual composition of metal component in the synthesized binary systems fits best the theoretically expected one (1: 1) for the PtAg/C catalyst whereas in the PtNi/C and PtCu/C systems, a considerable fraction of alloying component is present in the form of the corresponding oxides. A decrease in the average size of crystallites of metal component from 3.8 to 1.6 nm in the series of studied materials PtAg/C > Pt/C ≥ PtCu/C s> PtNi/C does not correspond to the character of the variation of electrochemically active surface area of the catalysts: PtNi/C ≈ PtCu/C < Pt/C ≪ PtAg/C increasing from 16–20 to 62–69 m2/g(Pt). The contradiction can be caused by the preferential segregation of platinum on the surface of nanoparticles of PtAg alloy, a higher degree of agglomeration of smaller nanoparticles, and, in the case of PtNi/C and PtCu/C materials, also by the insulation of a fraction of nanoparticle surface area by the corresponding oxides.