Formation of Black Silicon in a Process of Plasma Etching with Passivation in a SF6/O2 Gas Mixture

Publication typeJournal Article
Publication date2024-05-28
Journal: Nanomaterials
scimago Q1
SJR0.798
CiteScore8.5
Impact factor4.4
ISSN20794991
PubMed ID:  38869570
Abstract

This article discusses a method for forming black silicon using plasma etching at a sample temperature range from −20 °C to +20 °C in a mixture of oxygen and sulfur hexafluoride. The surface morphology of the resulting structures, the autocorrelation function of surface features, and reflectivity were studied depending on the process parameters—the composition of the plasma mixture, temperature and other discharge parameters (radical concentrations). The relationship between these parameters and the concentrations of oxygen and fluorine radicals in plasma is shown. A novel approach has been studied to reduce the reflectance using conformal bilayer dielectric coatings deposited by atomic layer deposition. The reflectivity of the resulting black silicon was studied in a wide spectral range from 400 to 900 nm. As a result of the research, technologies for creating black silicon on silicon wafers with a diameter of 200 mm have been proposed, and the structure formation process takes no more than 5 min. The resulting structures are an example of the self-formation of nanostructures due to anisotropic etching in a gas discharge plasma. This material has high mechanical, chemical and thermal stability and can be used as an antireflective coating, in structures requiring a developed surface—photovoltaics, supercapacitors, catalysts, and antibacterial surfaces.

Top-30

Journals

1
2
1
2

Publishers

1
2
1
2
  • We do not take into account publications without a DOI.
  • Statistics recalculated only for publications connected to researchers, organizations and labs registered on the platform.
  • Statistics recalculated weekly.

Are you a researcher?

Create a profile to get free access to personal recommendations for colleagues and new articles.
Share
Cite this
GOST | RIS | BibTex | MLA
Found error?