Theoretical analysis of the factors, influencing composition uniformity of the cadmium zinc telluride substrates grown by THM

The effect of the sample composition, variation of the temperature field and the feed material non-homogeneity on uniformity of the growing crystal is considered. It is shown that optimization of the solvent composition makes it possible to minimize the jump of the ZnTe concentration at the seed/crystal boundary. The composition fluctuations at variation of the thermal field during crystal growth are smooth enough and relatively non-significant. The feed composition distribution has, as a rule, a random character. Different harmonics of composition distribution non-uniformity in the feed material differently affect the homogeneity of the growing crystal. Longwave non-uniformities in the feed transform into the growing crystal almost completely. At the wavelength equals to a half of the solvent length or shorter, the perturbations of the growing crystal composition are relatively small. Evidently, the cause of the local composition variations, found in real crystals, is, basically, the feed composition non-uniformities