A new coating for improving the electrochemical performance of cathode materials

The layered LiNi 0.40 Mn 0.40 Co 0.20 O 2 compound was synthesized and modified with a mixed alumina–carbon coating by a simple soft chemical route. The simultaneous presence of alumina and carbon on the surface of coated samples was proved by ICP-AES, chemical analysis, XP spectroscopy, SEM microanalysis and local electron diffraction. For the first time, we show that the alumina epitaxial layer is formed on basal {001} facets of cathode grains, whereas side-view facets, like {010}, remain free from crystalline α-Al 2 O 3 , thus leaving them easy for Li-ion diffusion into cathode structure. An amorphous carbon film was used here for better conductivity of the coating layer and prevention of the electrical contact loss between cathode grains. Electrochemical tests revealed that the mixed alumina-carbon coating applied on LiNi 0.40 Mn 0.40 Co 0.20 O 2 stabilizes the surface structure and improves the cycling performance (3–4.5 V) and rate capability of cathodes on their basis compared with the pristine and alumina-coated LiNi 0.40 Mn 0.40 Co 0.20 O 2 samples.