Structure and Properties of the Electroexplosive Coating of the TiB2-Ag System after Electron Beam Treatment

A coating of the TiB₂-Ag system was formed through the use of sequential operations of electroexplosive spraying and electron beam processing. The values of electrical conductivity (62.0 MS/m), Vickers microhardness (0.251-0.265 GPa at the point of measurement on a silver matrix and 25-32 GPa at the point of measurement at inclusions of boride phases), nanohardness (4.48 ± 0.76 GPa) were determined), Young’s modulus (116±29 GPa), wear parameter under dry friction-sliding conditions (1.2 mm³/N • m) and friction coefficient (0.5). Switching wear resistance during accelerated tests was 7000 on and off cycles with an electrical resistance of 10.01 - 11.76 LiOhm. The thickness of the coatings is 100 microns. The coatings are formed by a silver matrix with inclusions of titanium borides located in it with three types of sizes: nanocrystalline, submicrocrystalline and microcrystalline. Quantitatively, in the structural composition among titanium borides, titanium diboride and silver (56 wt. %) are formed predominantly (41 wt. %), while other titanium borides account for 3 wt. %. Structural transformations are described using complementary methods of X-ray phase analysis, scanning and transmission electron microscopy.