Crystal structure refinement and reflectance measurements of hausmannite, Mn3O4

SummaryThe crystal structure of hausmannite from Langbån, Sweden, was refined with 462 independent X-ray diffraction data toR = 0.036 (RW = 0.034). The Jahn-Teller distortion of the Mn3+O6 octahedron is relatively strong: Mn3+ -O = 1.930 (1) Å (4 x), 2.282 (1) Å (2 x), and the anisotropies of the thermal vibrations of Mn3- and O differ clearly from those of the corresponding atoms in cubic spinels. It is shown that, from a stereochemical point of view, the hausmannite structure-type is not the only geometrically possible Jahn-Teller distortion of the spinel-type. The reflectance of hausmannite was measured on an oriented cut plate with polarized light (k = 400–700 nm) in air and in oil immersion, and the refractive indices and absorption coefficients were derived.ZusammenfassungDie Kristallstruktur eines Hausmannits von Langbån, Schweden, wurde an Hand von 462 unabhängigen Einkristall-Röntgendiffraktometerdaten zu einemR = 0.036 (Rw = 0.034) verfeinert. Die Jahn-Teller-Verzerrung des Mn3+O6-Oktaeders ist relativ stark: Mn3--O = 1.930 (1) Å (4 x); 2.282 (1) Å (2 x), und die Anisotropien der thermischen Schwingungen von Mn3 und O unterscheiden sich deutlich von denen analoger Atome in kubischen Spinellen. Es wird gezeigt, daß aus einer stereochemischen Sicht der Strukturtyp des Hausmannits nicht die einzig geometrisch mögliche JahnTeller-Verzerrung des Spinell-Typs ist. Das Reflexionsvermögen des Hausmannits wurde an einer orientiert geschnittenen Platte mit polarisiertem Licht (λ = 400–700 nm) in Luft und in Ölimmersion gemessen und Brechungsindizes und Absorptionskoeffizienten wurden bestimmt.