The hydrodechlorination of chlorobenzene in the vapor phase in the presence of metal-carbon nanocomposites based on nickel, palladium, and iron

Metal-carbon nanocomposites based on nickel, palladium, and iron and bimetallic palladium-nickel-carbon nanocomposites were for the first time used as catalysts of hydrodechlorination of chlorobenzene in the vapor phase in the atmosphere of hydrogen. Nickel and Pd-Ni nanoparticles completely coated by a carbon layer not only were stable to oxidation and agglomeration but also exhibited considerable activity in hydrodechlorination of chlorobenzene at temperatures much lower than those at which dechlorination on carbon carriers occurred. The dependence of catalytic properties (activity, selectivity, and stability) on temperature and nanocomposite composition was studied. Depending on the nature of the metal, the composition of bimetallic particles and temperature the selectivity could be changed, and the reaction could be directed toward the formation of benzene or cyclohexane. Carbon coating was stable under reaction conditions at least up to 350°C and did not hinder hydrodechlorination. Substrate adsorption likely occurred on the outside carbon surface of composite particles. The activity and structure of Ni@C composite remained almost unchanged after triple cycling over the temperature range from 50 to 350°C in a flow system.